性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 模收缩 | 1.2-1.4 | |||
比重 | ASTM D-792 | 1.34 | |||
自燃性 | UL-94 | HB | |||
吸水量 | 50相对湿度 | ASTM D-570 | 0.35 | ||
吸水量 | 24小时浸渍 | ASTM D-570 | 0.43 | ||
吸水量 | 浸渍平衡点 | ASTM D-570 | 0.85 | ||
机械性能 | 拉伸强度 | 100 | |||
ASTM D-638 | >17 | MPa | |||
拉伸强度 | -55 | ||||
ASTM D-638 | 99 | MPa | |||
IZOD冲击试验 | 缺口-40 | ||||
ASTM D-256 | 249 | j/m | |||
挠曲系数 | 100 | ||||
ASTM D-790 | 340 | MPa | |||
破裂点拉伸变形量 | 122 | ||||
ASTM D-638 | >480 | ||||
洛氏硬度M | ASTM D-785 | 58 | |||
抗拉伸冲击强度 | 长试片23 | ||||
ASTM D-1822 | 1590 | kj/m2 | |||
压缩应力 | 23,10变形 | ASTM D-695 | 52 | MPa | |
洛氏硬度R | ASTM D-785 | 105 | |||
挠曲系数 | -55 | ||||
ASTM D-790 | 3260 | MPa | |||
拉伸强度 | 70 | ||||
ASTM D-638 | >29 | MPa | |||
破裂点拉伸变形量 | 100 | ||||
ASTM D-638 | >580 | ||||
挠曲系数 | 122 | ||||
ASTM D-790 | 230 | MPa | |||
破裂点拉伸变形量 | 70 | ||||
ASTM D-638 | >498 | ||||
破裂点拉伸变形量 | -55 | ||||
ASTM D-638 | 455 | ||||
IZOD冲击试验 | 23 | ||||
ASTM D-256 | 901 | j/m | |||
抗剪强度 | 23 | ||||
ASTM D-732 | 34 | MPa | |||
破裂点拉伸变形量 | 23 | ||||
ASTM D-638 | 521 | ||||
挠曲系数 | 23 | ||||
ASTM D-790 | 1280 | MPa | |||
挠曲系数 | 70 | ||||
ASTM D-790 | 650 | MPa | |||
压缩应力 | 23,1变形 | ASTM D-695 | 8 | MPa | |
挠曲变形强度 | 23 | ||||
ASTM D-790 | 40 | MPa | |||
挠曲疲劳忍耐限度 | 50RH,23,106周期 | ASTM D-671 | 16 | MPa | |
拉伸强度 | 23 | ||||
ASTM D-638 | 64 | MPa | |||
弹性系数 | 23 | ||||
ASTM D-638 | 1280 | MPa | |||
拉伸强度 | 122 | ||||
ASTM D-638 | >11 | MPa | |||
负载变形量 | 140kg/cm2,50 | ||||
ASTM D-621 | 3.0 | ||||
电气性能 | 容积电阻率 | 23,0.2含水量 | ASTM D-257 | 2.3×1014 | Ω.cm |
介电因数 | 50RH,23,106Hz | ASTM D-150 | 0.007 | ||
抗电弧 | 3.1mm | ASTM D-495 | 120 | sec | |
介电强度 | 瞬间Short time(2.3mm) | ASTM D-149 | 19.9(2.3) | kv/mm | |
介电常数 | 50RH,23,102106Hz | ASTM D-150 | 4.1 | Ω.cm | |
热性能 | 热畸变温度 | 0.5MPa | ASTM D-648 | 168 | |
热畸变温度 | 1.8MPa | ASTM D-648 | 65 | ||
线性热膨胀系数 | 104160 | ||||
ASTM D-696 | 12.8 | 10-5m/m | |||
线性热膨胀系数 | -4029 | ||||
ASTM D-696 | 9.9 | 10-5m/m | |||
线性热膨胀系数 | 60104 | ||||
ASTM D-696 | 9.7 | 10-5m/m | |||
线性热膨胀系数 | 2960 | ||||
ASTM D-696 | 10.6 | 10-5m/m | |||
熔点 | ASTM D-2133 | 175 |
供应POM 美国杜邦 100ST 共聚甲醛 增韧级 耐磨 高抗冲 汽车部件