牌号 加工级别 ..
现货供应奥升德R413H，是一种通用型、抗冲击改性的 15% 玻璃纤维增强型聚酰胺 66 树脂。具有出色的热稳定性。这款材料的设计在保持物理特性的同时 限度地提高了韧性。此外，该产品经润滑改性，流动性得以提升，让制件拥有更优异的外观质量。可用于汽车紧固件，高压线束护板。
奥升德PA66 R413H物性表：
| Physical | Dry | Conditioned | Unit | Test Method |
Density | 1.21 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow : 23°C, 2.00 mm | 0.80 | -- | % | |
Flow : 23°C, 2.00 mm | 0.70 | -- | % | |
Water Absorption (24 hr, 23°C) | 1.0 | -- | % | ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus (23°C) | 5500 | 4100 | MPa | ISO 527-1 |
Tensile Stress (Break, 23°C) | 110 | 80.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 5.0 | 13 | % | ISO 527-2 |
Flexural Modulus (23°C) | 4800 | 2800 | MPa | ISO 178 |
Flexural Stress (23°C) | 140 | 73.0 | MPa | ISO 178 |
Poisson's Ratio (23°C) | 0.40 | -- | ISO 527-2 | |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-40°C | 5.0 | 5.0 | kJ/m² | |
-30°C | 6.0 | 10 | kJ/m² | |
23°C | 12 | 18 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 75 | 70 | kJ/m² | |
23°C | 80 | 76 | kJ/m² | |
Notched Izod Impact Strength | ISO 180/1A | |||
-40°C | 9.0 | 9.0 | kJ/m² | |
-30°C | 10 | 10 | kJ/m² | |
23°C | 12 | 21 | kJ/m² | |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 258 | -- | °C | ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 235 | -- | °C | ISO 75-2/A |
Melting Temperature | 260 | -- | °C | ISO 11357-3 |
CLTE - Flow (23 to 55°C, 2.00 mm) | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
CLTE - Transverse (23 to 55°C, 2.00 mm) | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
RTI Elec | UL 746B | |||
0.40 mm | 120 | -- | °C | |
0.75 mm | 130 | -- | °C | |
1.5 mm | 130 | -- | °C | |
3.0 mm | 130 | -- | °C | |
RTI Imp | UL 746B | |||
0.40 mm | 85.0 | -- | °C | |
0.75 mm | 85.0 | -- | °C | |
1.5 mm | 85.0 | -- | °C | |
3.0 mm | 85.0 | -- | °C | |
RTI Str | UL 746B | |||
0.40 mm | 125 | -- | °C | |
0.75 mm | 125 | -- | °C | |
1.5 mm | 125 | -- | °C | |
3.0 mm | 125 | -- | °C | |
| Electrical | Dry | Conditioned | Unit | Test Method |
Volume Resistivity (1.00 mm) | 1.0E+11 | -- | ohms·cm | IEC 60093 |
Electric Strength (1.00 mm) | 3.0 | -- | kV/mm | IEC 60243-1 |
Arc Resistance (3.00 mm) | PLC 6 | -- | ASTM D495 | |
Comparative Tracking Index (3.00 mm) | 400 to 599 | -- | V | IEC 60112 |
High Amp Arc Ignition (HAI) | UL 746A | |||
0.40 mm | PLC 1 | -- | ||
0.75 mm | PLC 1 | -- | ||
1.5 mm | PLC 1 | -- | ||
3.0 mm | PLC 1 | -- | ||
High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 3 | -- | UL 746A | |
Hot-wire Ignition (HWI) | UL 746A | |||
0.40 mm | PLC 4 | -- | ||
0.75 mm | PLC 4 | -- | ||
1.5 mm | PLC 4 | -- | ||
3.0 mm | PLC 4 | -- | ||
| Flammability | Dry | Conditioned | Unit | Test Method |
Flame Rating | UL 94 | |||
0.75 mm | HB | -- | ||
1.5 mm | HB | -- | ||
3.0 mm | HB | -- |