1100-630S台湾长春PBT塑胶原料增韧汽车连接器用，适合高拉拨力要求。原厂原包，提供原厂质量检验证书(COA)，1100-630S物性表等资料。
PBT 1100-630S物性表：
| Physical | Nominal Value | Unit | Test Method |
Density | 1.31 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.6 to 1.8 | % | |
Flow | 1.8 to 2.0 | % | |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 2200 | MPa | ISO 527-1 |
Tensile Stress (Break, 23°C) | 55.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 60 | % | ISO 527-2 |
Flexural Modulus (23°C) | 2200 | MPa | ISO 178 |
Flexural Stress (23°C) | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 155 | °C | ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
Electric Strength (2.00 mm) | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | HB | UL 94 |
| Processing Information | |||
| Injection | Nominal Value | Unit | |
Drying Temperature | 120 to 140 | °C | |
Drying Time | 4.0 | hr | |
Processing (Melt) Temp | 240 to 270 | °C | |
Mold Temperature | 60 to 100 | °C | |